WC-Co Powder ine yakasimba Wear-Resistance
Tsanangudzo
WC-Co Hupfu:Zvishandiso zvepamusoro-soro zveMaapplication Asingapfeki
Kuunza huwandu hwedu hweWC-Co hupfu, hwakagadzirirwa kupa kusarudzika kupfeka kuramba uye kusimba mumhando dzakasiyana dzemaindasitiri ekushandisa.Hupfu hwedu hwakagadzirwa netungsten carbide (WC) zvidimbu zvakabatanidzwa necobalt (Co) binder, zvichikonzera chinhu chakaoma uye chakaoma.
Chigadzirwa chedu chinosanganisira mamakisi mana makuru: KF-60 WC-12Co, KF-61 WC-17Co, uye KF-62 WC-25Co, imwe neimwe ine zvakasiyana-siyana cobalt zvemukati uye particle size kugovera.KF-60 inowanikwa mune ese ari maviri sintered uye akapwanyika kana agglomerated uye sintered mafomu, ane particle size inotangira 15-45μm uye 10-63μm, zvichiteerana.KF-61 uye KF-62 ese ari agglomerated uye sintered hupfu, ane particle saizi kubva 15-45μm uye 10-38μm.
Yedu WC-Co poda inopa yakanakisa kupfeka kuramba uye inonyanya kukodzera maapplication uko kune yakakwira mwero wekupokana, senge mumakina akajairwa kana mafambiro ekupfeka.Iyo yakakwira cobalt yemukati muKF-61 uye KF-62 inopa kuomarara kuri nani, ichiita kuti ive yakanakira maapplication uko kunokanganisa kuramba kunodiwa zvakare.
Pamusoro pekuramba kwavo kupfeka kwakasarudzika, yedu WC-Co hupfu zvakare inosiyana-siyana uye inogona kushandiswa nenzira dzakasiyana siyana.Anogona kupfapfaidzwa panzvimbo kuti agadzire bhachi rakaomarara uye risingapfeki, kana kuti anogona kushandiswa kugadzira zvinhu zvisingapfeke senge maturusi ekucheka, mabhengi, uye zvisimbiso.
Kunzvimbo yedu yemazuva ano yekugadzira, tinoshandisa nzira dzepamusoro dzekugadzirisa kuti tive nechokwadi chekuenderana uye chepamusoro-soro poda.Zvigadzirwa zvedu zvinoyedzwa zvine hukasha kuti ive nechokwadi chekuti zvinosangana nemhando yepamusoro yekuramba kupfeka uye kusimba.
Muchidimbu, huwandu hwedu hweWC-Co hupfu isarudzo yakavimbika kune maindasitiri ekushandisa uko kupfeka kuramba uye kusimba kwakakosha.Nezvimiro zvavo zvakasarudzika uye kuita kwakasiyana-siyana, vanopa mhinduro inodhura yekuwedzera hupenyu hwezvikamu nekuvandudza mashandiro emuchina.
Zvigadzirwa zvakafanana
| Brand | Product Name | AMPERIT | METCO/AMDRY | WOKA | PRAXAIR | PAC |
| KF-60P | WC-12Co | 515 | 72F-NS | WC-114WC-489-1 | 127 | |
| WC-12Co | 518519 | 3101-3106 | WC-7271342 | 125126 127 | ||
| KF-60C | WC-12Co(Low Carbon) | 512 | ||||
| KF-61P | WC-17Co | 526 | 5143 2005NS 73F-NS | 32023202 | WC-7291343 | |
| KF-62 | WC-25Co |
Tsanangudzo
| Brand | Product Name | Chikamu Chekukura (μm) | Chemistry (wt%) | Type | Density inooneka | Kuyerera | Properties | Application | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Co | C | Fe | W | Cr | B | Si | Ni | ||||||||
| KF-65 | WC-10Co4Cr | 15-45, 10-38 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Sinter&Crush | 5.5-6.5g/cm3 | ≤25 s/50g | APS, HVOF, HVAF | Alternative hard chromium plating;Petroleum, bepa, general muchina | |||
| KF-65 | WC-10Co4Cr | 15-45,10-38,5-30 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated uye sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVOF, HVAF | Alternative hard chromium plating;Petroleum, bepa, general muchina | |||
| KF-65 | WC-10Co4Cr | 5-25,5-15 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated uye sintered | 3.5-4.8 g/cm3 | Kudyisa kwakagadzikana kune upfu | HVOF,HVAF | Alternative yakaoma chromium plating; | |||
| KF-60 | WC-12Co | 15-45, 10-63 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Sinter&Crush | 5.5-6.5 g/cm3 | ≤25 s/50g | APS, HVOF | Pfeka kuramba，Kunetseka kupfeka kuramba | ||||
| KF-60 | WC-12Co | 15-45, 10-38,5-30 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Agglomerated uye sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVOF, HVAF | Pfeka kuramba, Fretting kupfeka kuramba; general muchina | ||||
| KF-61 | WC-17Co | 15-45, 10-38 | 15.5-17 | 4.5-5.1 | ≤0.8 | Bal. | Agglomerated uye sintered | 3.5-5.5 g/cm3 | ≤25 s/50g | APS, HVOF, HVAF | Pfeka kuramba, Fretting kupfeka kuramba, Zvirinani kuoma; general muchina | ||||
| KF-62 | WC-25Co | 15-45, 10-38 | 22-26 | 4.0-4.6 | ≤0.8 | Bal. | Agglomerated uye sintered, Densification | 3.0-5.5 g/cm3 | ≤25 s/50g | APS, Detonation pfuti, kupfapfaidza inotonhora | Fretting kupfeka resistance，Zviri nani kuomarara | ||||
| KF-66 | WC-23%CrC-7Ni | 15-45, 10-38 | 6.0-6.8 | ≤0.8 | Bal. | 16.5-20 | 5.5-7 | Agglomerated uye sintered | 3.0-5.0 g/cm3 | ≤25 s/50g | APS, HVOF, HVAF | Alternative hard chromium plating; Inoshandiswa kune yakaderera concentration acid/alkali nharaunda pa200 ℃;Anti oxidation uye kupfeka kuramba pa750 ℃ | |||
| KF-66 | 43WC-43%CrC-14Ni | 15-45,10-38 | 7.8-8.4 | ≤0.8 | Bal. | 35-38 | 12-14 | Agglomerated uye sintered | 2.0-4.0 g/cm3 | ≤35 s/50g | APS, HVOF, HVAF | Alternative hard chromium plating Inoshandiswa kune yakaderera concentration acid/alkali nharaunda pa200 ℃. | |||
| KF-63 | WC-10Ni | 15-45,10-38 | 4.5-5.2 | ≤0.1 | Bal. | 8.5-10.5 | Agglomerated uye sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVF, HVAF | Non magineti kupfeka resistant coating.Zvirinani kuonda kwegora | ||||
| KF-70 | Cr3C2-25NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 18-21.5 | Agglomerated uye sintered | ≥2.3 g/cm3 | Kudyisa kwakagadzikana kune upfu | APS, HVOF | Anti oxidation uye kupfeka kuramba pa815 ℃ | ||||
| KF-69 | Cr3C2-20NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated uye sintered | ≥2.3 g/cm3 | Kudyisa kwakagadzikana kune upfu | APS, HVOF | Anti oxidation uye kupfeka kuramba pa815 ℃ | ||||
| KF-71 | Cr3C2-30NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated uye sintered | ≥2.3 g/cm3 | Kudyisa kwakagadzikana kune upfu | APS, HVOF | Anti oxidation uye kupfeka kuramba pa815 ℃.Kuoma kuri nani | ||||
| KF-60 | WC-12Co (Low Carbon) | 15-45, 20-53 | 10.5-12 | 4.0-4.4 | ≤0.8 | Bal. | Agglomerated uye sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | HVOF,HVAF | Inoshandiswa kuZn bath rolls muContinuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-10Co | 15-45,20-53,10-38 | 9-11 | 3.5-3.9 | Bal. | 1.4-1.7 | Agglomerated uye sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Inoshandiswa kuZn bath rolls muContinuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-5Co5Cr | 15-45,20-53,10-38 | 4-6 | 3.5-3.9 | Bal. | 4-6 | 1.4-1.7 | Agglomerated uye sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Inoshandiswa kuZn bath rolls muContinuous Galvanizing Lines | |||
| KF-300E | 35%WC-NiCrBSi | 15-53,45-104 | 2.5-3.2 | 1.0-2.6 | 32-35 | 7.5-9 | 1.5-1.9 | 2.0-2.7 | Bal. | WC uye NiCrBSi kugadzira alloy | 4.0-4.9 g/cm3 | ≤16 s/50g | HVOF, PS | Alternative Blended type WC+Ni60;Kushandiswa kwezvinhu zvepamusoro,Kuderedza simba rekushandisa, kuderera kwekushisa;Inoshandiswa kugadzira girazi mold. | |
| KF-300F | 50% WC-NiCrBSi | 15-53,45-104 | 3.2-4.3 | 0.8-2.0 | 45-48 | 5.8-7.2 | 1.0-1.7 | 1.5-2.4 | Bal. | WC uye NiCrBSi kugadzira alloy | 5.0-7 g/cm3 | ≤16 s/50g | HVOF, PS | Alternative Blended type WC+Ni60;Kushandiswa kwezvinhu zvepamusoro,Kuderedza simba rekushandisa, kuderera kwekushisa;Inoshandiswa kugadzira girazi mold. | |